Comparison of Isothermal Oxidation Behavior of Co-10Cr-xSi(x=0,5,10)Alloys at 1 073K

Junhuai Xiang;Ling Wang;Honghua Zhang;Lingyun Bai;Changjun Wan;Ganlan Yang;Jiangxi Key Laboratory of Surface Engineering,Jiangxi Science and Technology Normal University;

The oxidation behavior of Co-10 Cr-xSi(x=0,5,10,nominal composition,at%)alloys in 0.1 MPa pure O2 at 1 073 Kwas investigated.Co-10 Cr presents the worst oxidation resistance with the mass gain of about 7.531 mg/cm2 after 24 hoxidation,while Co-10 Cr-10 Si presents the best oxidation resistance with the much lower mass gain of about 0.078 mg/cm2.Co-10 Cr-10 Si is about two magnitudes lower than that of Co-10 Cr.The oxidation behavior of Co-10 Cr-5 Si is intermediate between that of Co-10 Cr and Co-10 Cr-10 Si.The nodular oxides have occupied most of the alloy surface,and their microstructure is similar to Co-10 Cr,to some extent.On the contrary,only a fraction of the surface is covered by the Cr2 O3 layer,whose microstructure is similar to that of Co-10 Cr-10 Si.

CAJViewer7.0 supports all the CNKI file formats; AdobeReader only supports the PDF format.

评论
添加红包

请填写红包祝福语或标题

红包个数最小为10个

红包金额最低5元

当前余额3.43前往充值 >
需支付:10.00
成就一亿技术人!
领取后你会自动成为博主和红包主的粉丝 规则
hope_wisdom
发出的红包
实付
使用余额支付
点击重新获取
扫码支付
钱包余额 0

抵扣说明:

1.余额是钱包充值的虚拟货币,按照1:1的比例进行支付金额的抵扣。
2.余额无法直接购买下载,可以购买VIP、付费专栏及课程。

余额充值