Hastelloy c-276 alloy Physical Data

Hastelloy c-276 alloy Physical Data

Equal material :W.Nr.2.4610, NiMo16Cr16Ti, UNS N06455, NiMo16Cr16Ti 

Hastelloy C-276 material is a kind of Ni-Cr-Mo alloy containing tungsten with very low content of the silicon and carbon.

Hastelloy C-276 Characteristic: in oxidizing and reducing conditions, Hastelloy C-276  has excellent corrosion resistance to most corrosive medium. the excellent Corrosion resistance, crevice corrosion and stress corrosion cracking performance.JOIN WIN is Hastelloy C-276 manufacturer,we can supply Hastelloy C-276 alloy.

Hastelloy c-276 Chemistry Data:

	Ni	Cr	Fe	C	Mn	Si	Mo	W	Co	V	P	S
minimum	balance	15.0	4.0				15.0	3.0		0.1
maximum		16.5	7.0	0.01	1.0	0.08	17.0	4.5	2.5	0.3	0.015	0.01

Hastelloy c-276 alloy Physical Data:

Density: 8.89 g/cm3 (0.321 lbs/in2)

 

Exceptional Properties: corrosion resistance

Hastelloy C-276 corrosion-resisting alloy steel application:

Hastelloy C-276 has been widely used in chemical and petrochemical, such as element application chloride containing organic compounds in contact and catalytic

 system. This material is particularly suitable for high temperature, mixed with inorganic acid and organic acid impurities (such as formic acid and acetic acid),

 the use of seawater corrosion environment.

Other special applications:

The pulp and paper industry, such as cooking and bleaching solution container

The FGD system in the washing tower, heater, fan, wet steam

Equipment and components, work in the acidic gases in the environment

Reactor, acetic acid and acidic products

sulfuric acid condenser

methylene two phenyl isocyanate (MDI)

impure phosphoric acid production and processing

If you have a need, please contact us and give you the most professional service! We can supply Hastelloy C-276.

william(at)steel-jw(dot)com

Url www(dot)c267steel(dot)com

www(dot)x80pipeline(dot)com

www(dot)steel-jw(dot)com

Tel 86,371,63332179

来自 “ ITPUB博客 ” ，链接：http://blog.itpub.net/29531879/viewspace-1137122/，如需转载，请注明出处，否则将追究法律责任。

转载于:http://blog.itpub.net/29531879/viewspace-1137122/