Organopolysilazane (room temperature curing coating resin) IOTA-OPSZ-9150

Description:

The product has a unique Si-NH-Si bond, can be cured at room temperature, curing mainly involved in the reaction of Si-NH-Si hydrolysis and oxidation. While the Si-NH-Si bond and the substrate surface-OH easily react, and bring the substrate and good adhesion. Addition the appropriate catalyst in the resin can promote Si-H and Si-NH-Si reaction, after curing resin to form three-dimensional cross-linked structure, giving the material good mechanical properties, hardness can be as high as 9H.

OPSZ-9150 can anti-alcohol, ketones and other organic solvents after curing with.

Features:

Non-combustible (after curing)

Room temperature curing

Good persistence

Index:

Solid content: 100%

Viscosity: 50 cPs

Density after curing: 1.3 g / ml

Fully cured (20-25 ° C): 3 days

Room temperature curing for 1 day: 4H

Room temperature 3 hours, 120 degrees 2h: 8H

Water contact angle: 105 °

Applications:

Silicone curing agent

Package:

Cleaning:

OPSZ-9150 cured, ordinary solvents can’t be washed away. Can be used strong alkali, such as sodium hydroxide 10% aqueous solution soak for 5 hours or more to remove.

Shelf life: 2years; after the application, it depend on the protective measures, sealed low temperature drying case, the applicable period of more than half a year.

In a ventilated, dry environment, and use the necessary protective measures, such as gloves, masks, goggles.

After opening, seal it in a timely manner. If it is used in a humid environment, replace the container with nitrogen after using.