data

Table6 Electrochemical parameters obtained from potential dynamic polarization measurements after 15 days’ immersion of samples.
Immersion
time Electrochemical corrosion measurements
E_corr
(V/SCE) R_P
(MΩ∙〖cm〗^2) β_a
(V/dec) β_c
(V/dec) I_corr
(μA/〖cm〗^2) Corrosion rate
(mm/year)
2 -0.91 0.00065 0.50 0.23 104.92 1.51
3 -1.14 0.000020 0.43 0.23 3224.55 46.38
4 -1.21 0.000084 0.27 0.24 663.30 9.54
8 -1.20 0.000088 0.52 0.23 795.68 11.44
15 -1.09 0.00028 0.62 0.40 377.08 5.42
16 -1.07 0.00067 0.97 0.29 143.80 2.07
17 -1.08 0.0011 0.82 0.28 82.69 1.19
21 -1.04 0.0029 0.95 0.26 30.76 0.44
22 -1.07 0.0028 1.20 0.26 32.72 0.47
25 -1.06 0.0032 0.98 0.24 26.46 0.38
28 -1.01 0.0045 0.77 0.26 18.77 0.27
30 -1.01 0.0052 0.71 0.26 16.14 0.23
37 -1.07 0.0055 1.11 0.23 15.18 0.22
38 -1.06 0.0059 1.38 0.24 14.91 0.21
56 0.04 0.017 0.56 0.35 5.40 0.078



30:60:2%
  
30:30:2%与30:60:2%的对比
Table6 Electrochemical parameters obtained from potential dynamic polarization measurements after 15 days’ immersion of samples.
Immersion
time Electrochemical corrosion measurements
E_corr
(V/SCE) R_P
(MΩ∙〖cm〗^2) β_a
(V/dec) β_c
(V/dec) I_corr
(μA/〖cm〗^2) Corrosion rate
(mm/year)
0 -1.20 0.00015 0.563 0.252 14.00 0.20
1 -1.14 0.00040 0.220 0.209 3.31 0.048
6 -1.14 0.00021 0.356 0.369 10.57 0.15
8 -1.17 0.00015 0.458 0.260 13.83 0.20
9 -1.09 0.00018 0.517 0.395 15.86 0.23
10 -0.84 0.0018 0.309 0.238 0.95 0.014
13 -0.88 0.0019 0.392 0.223 0.91 0.013
16 -0.82 0.0029 0.278 0.214 0.51 0.0074
17 -0.88 0.0030 0.342 0.0920 0.30 0.0043
20 -0.61 0.0020 0.541 0.122 6.05 0.0025