C72700铜基合金热处理问题（铜镍锡合金）

1. 网上搜集的资料：

 网址： Copper-Nickel Alloy (UNS C72700)

Fabrication

Welding - Soldering, seam welding, butt welding, spot welding, brazing, and gas shielded arc welding are excellent techniques.

Forging - The hot forging temperature for copper UNS C72700 alloy ranges between 649 and 871ºC (1200 and 1600ºF).

Hot working - Copper UNS C72700 alloy has good hot working abilities.

Cold working - Copper UNS C72700 alloy has excellent cold working properties.

Annealing - Copper UNS C72700 alloy can be annealed at 732ºC (1350ºF).

翻译： 制作
焊接——钎焊、缝焊、对焊、点焊、钎焊和气体保护电弧焊都是优秀的技术。
锻造-铜UNS C72700合金的热锻温度范围在649至871ºC（1200至1600ºF）之间。
热加工-铜UNS C72700合金具有良好的热加工能力。
冷加工-铜UNS C72700合金具有优异的冷加工性能。
退火-铜UNS C72700合金可以在732ºC（1350ºF）下退火。

2. 网上资料：

Texture and Special Grain Boundary Distribution of C71500 Copper-Nickel Alloy Tubes at Different Annealing Temperatures | Journal of Materials Engineering and Performance

Two-stage rolling process was adopted to study the texture and special grain boundary distribution of C71500 copper-nickel alloy tubes at different annealing temperatures. The effect of temperature on the texture of C71500 copper-nickel alloy tube was analyzed. The hardness analysis was used to study the recrystallization and low lattice reconstruction grain boundaries ratio at different temperatures. It was observed by electron backscattered diffraction that static recovery of the alloy tube occurs when the annealing temperature below 800 °C and it transforms into static recrystallization at 825 °C. The initial strain-induced grain boundary migration temperature of alloy tube is about 775 °C. The number of Copper{112}<111> textures can be used to determine the ratio of the low coincidence site lattice (low ΣCSL) grain boundary. The optimal annealing process for C71500 alloy tube to obtain a high proportion of special grain boundaries is to keep the temperature at 800 °C for 15 min.

采用两阶段轧制工艺研究了C71500铜镍合金管材在不同退火温度下的织构和特殊晶界分布。分析了温度对C71500铜镍合金管材织构的影响。采用硬度分析法研究了不同温度下的再结晶和低晶格重构晶界比。通过电子背散射衍射观察到，当退火温度低于800°C时，合金管发生静态恢复，并在825°C时转变为静态再结晶。合金管的初始应变引起晶界迁移温度约为775°C。铜{112}<111>织构的数量可以用来确定低符合位晶格（低∑CSL）晶界的比率。C71500合金管获得高比例特殊晶界的最佳退火工艺是将温度保持在800°C 15分钟。

3. 网上资料：

AMS 4597 C72900 Alloy, C729 Copper Nickel-Tin Bronze - Concast Metal Products Co.

Thermal Properties

Treatment	Minimum*	Maximum*
Thermal Properties provided by CDA   *Temperature is measured in Fahrenheit.
Annealing	1515 /  824 摄氏度
Hot Treatment	1200 / 649 摄氏度	1600

4. 在网上搜集资料的过程中发现，国内道客88文库里面也有相关的论文，主要是材料关键字需要是：Cu_9Ni_6Sn， 与国内一般材料命名方法不一样，国内一般是CuNi9Sn6，需要注意；

Cu_9Ni_6Sn弹性铜合金的组织及性能研究 - 道客巴巴

喷射沉积法Cu_9Ni_6Sn合金的组织与性能研究 - 道客巴巴

Cu-9Ni-6Sn合金概述 - 道客巴巴